Aluminum (AlSi₁₀Mg)

The strength, thermal properties, low weight, and flexible post-processing of this aluminum alloy, AlSi₁₀Mg, make it a favorite for prototyping and manufacturing — especially in industries like automotive, aerospace, and automation. With this alloy, users can create larger models than with any other metal 3D printing material.

Get an instant quote

Talk to our team

Two 3D-printed metal grippers with a design optimized for 3D printing

技術仕様

Maximum part dimensions	500 x 280 x 345 mm 500 x 280 x 325 mm (online orders)
Standard accuracy	Better than or equal to the industry standards: DCTG 6 of DIN EN ISO 8062-3 for dimensions between 0.5 and 30 mm DCTG 8 of DIN EN ISO 8062-3 for dimensions between 30 and 400 mm DIN ISO 2768-1 c (coarse) for dimensions between 0.5 mm and 400 mm See design guidelines for more information on standard accuracy.
Layer thickness	Standard: 0.09 mm, Performance: 0.06 mm
Minimum wall thickness	Standard: 1 mm, Performance: 0.5 mm
Minimum detail size	0.4 mm
Interlocking or moving parts	No
Internal channels	Yes
Surface structure	Rough surface

等級

各プロジェクトの実績と効率のバランスを標準または実績等級の選択で調整します。

Standard

The all-rounder, where it’s all about technology:

Ideal for prototypes and simple end-parts
Form-, fit-, and function-testing
Strength and density similar to cast parts
Industry-standard quality requirements

Performance

The specialist, for complex production:

Ideal for complex metal parts designed for AM
Preferred for applications in demanding environments
Suited for series production
Higher strength and density than casting
Specialized quality test reports available to your specification

データシート

パラメーター	標準グレード	パフォーマンス・グレード	標準	単位	方法
Density WGE-Prod-067EN	>2.59	g/cm³	WGE-Prod-067EN
Relative density WGE-Prod-067EN	>97.0	%	WGE-Prod-067EN
Tensile strength DIN EN ISO 6892-1:2009	>250	MPa	DIN EN ISO 6892-1:2009
Yield strength DIN EN ISO 6892-1:2009	>180	MPa	DIN EN ISO 6892-1:2009
Elastic modulus DIN EN ISO 6892-1:2009	70	GPa	DIN EN ISO 6892-1:2009
Elongation at break DIN EN ISO 6892-1:2009	>1.0	%	DIN EN ISO 6892-1:2009
Roughness R_a ISO 4287 / AITM 1-00070	<20	µm	ISO 4287 / AITM 1-00070
Roughness R_z ISO 4287 / AITM 1-00070	<80	µm	ISO 4287 / AITM 1-00070
Hardness ISO 6597-1:03-2006	>80	HV	ISO 6597-1:03-2006

Actual values may vary with build conditions.

Strong tensions due to part geometry may distort parts, potentially leading to greater deviation in values. Values for surface roughness depend on the orientation of the surface; downward-facing surfaces and surfaces with support will be rougher.

These values show the material characteristics without additional stress relief heat treatment. Extra heat treatment steps for even higher mechanical properties may be possible, e.g. for serial produced parts.

Please get in touch with our team for more information.

PDFをダウンロードする

Finishing degrees

The right finish can transform your print into a product. Explore the post-production finishes we offer for this material. If you have any questions or special requests, get in touch with us.

Supports removed

Corundum blasted (matte)