Titanium (Ti₆Al₄V)

Ti₆Al₄V is one of the most widely used alloys in metal 3D printing. It offers excellent mechanical strength, high strength-to-weight ratio, and superior corrosion resistance, making it an ideal choice for the aerospace, automotive, and medical industries. This material is highly suitable for functional prototypes, end-use parts, and spare parts.

Get an instant quote

Talk to our team

3D-printed lift bracket in titanium with holes for lightweightness

技術仕様

Maximum part dimensions	250 x 250 x 305 mm 250 x 250 x 275 mm (online orders)
Standard accuracy	Better than or equal to the industry standards: DCTG 6 of DIN EN ISO 8062-3 for dimensions between 0.5 and 30 mm DCTG 8 of DIN EN ISO 8062-3 for dimensions between 30 and 400 mm DIN ISO 2768-1 c (coarse) for dimensions between 0.5 mm and 400 mm See design guidelines for more information on standard accuracy.
Layer thickness	Standard: 0.06 mm, Performance: 0.03 mm
Minimum wall thickness	Standard: 1 mm, Performance: 0.5 mm
Minimum detail size	0.4 mm
Interlocking or moving parts	No
Internal channels	Yes
Surface structure	Rough surface

等級

各プロジェクトの実績と効率のバランスを標準または実績等級の選択で調整します。

Standard

The all-rounder, where it’s all about technology:

Ideal for prototypes and simple end-parts
Form-, fit-, and function-testing
Strength and density similar to cast parts
Industry-standard quality requirements

Performance

The specialist, for complex production:

Ideal for complex metal parts designed for AM
Preferred for applications in demanding environments
Suited for series production
Higher strength and density than casting
Specialized quality test reports available to your specification

データシート

パラメーター	標準グレード	パフォーマンス・グレード	標準	単位	方法
Density WGE-Prod-067EN	>4.36	g/cm³	WGE-Prod-067EN
Relative density WGE-Prod-067EN	>99	%	WGE-Prod-067EN
Tensile strength DIN EN2002-1	>900*	MPa	DIN EN2002-1
Yield strength DIN EN2002-1	>830*	MPa	DIN EN2002-1
Elastic modulus DIN EN2002-1	110	GPa	DIN EN2002-1
Elongation at break DIN EN2002-1	>10*	%	DIN EN2002-1
Roughness R_a ISO 4287 / AITM 1-00070	<20	µm	ISO 4287 / AITM 1-00070
Roughness R_z ISO 4287 / AITM 1-00070	<80	µm	ISO 4287 / AITM 1-00070
Hardness ISO 6597-1:03-2006	>310	HV	ISO 6597-1:03-2006

*Values for tensile specimens according to DIN EN ISO 6892 status as built

Actual values may vary with build conditions.

Strong tensions due to part geometry may distort parts, potentially leading to greater deviation in values. Values for surface roughness depend on the orientation of the surface; downward-facing surfaces and surfaces with support will be rougher.

These values show the material characteristics with additional stress relief heat treatment. Extra heat treatment steps, hot isostatic pressing (HIP), or aging for even higher mechanical properties may be possible, e.g. for serial-produced parts.

Please get in touch with our team for more information.